供应沙伯基础无卤阻燃级PPO改性聚苯醚 牌号SE1X
沙伯基础创新PPO NORYL™ SE1X 产品特性: 无卤阻燃 UL94V-0
NORYL®改进型PPO® 树脂是一类以聚苯醚 (有时称作聚环氧丙烷或
PPO )为基料的工程热塑性树脂。PPO,一种耐高温无定形聚合物,与聚
苯乙烯生成一种可混溶单相共混物。使用这种技术,伴以其他添加剂,
可制成一类物理和热力性能广泛的树脂。
除具有耐高温性、良好的机械性能和耐燃性外, NORYL 树脂还兼具设
计灵活性及范围广泛的加工选择特性。此类树脂的低吸湿性和耐水解性
— 所有工程热塑性塑料中最低 一 使树脂在湿度和温度条件变化很大
的情况下,仍具有良好的电性能。NORYL树脂热挠曲温度高达 380°F
(193°C), 辅以耐冲击强度和广泛的UL认可,它们被作为必须在高温负载
下运行的制件的设计替代品。
沙伯基础创新PPO SE1X 产品物性表:
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.09
|
g/cm3
|
ASTM D792 |
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg)
|
8.5
|
g/10 min
|
ASTM D1238 |
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg)
|
8.70
|
cm3/10min
|
ISO 1133 |
Molding Shrinkage - Flow (3.20 mm)
|
0.50 to 0.70
|
%
|
Internal Method |
Molding Shrinkage - Across
Flow 2
|
0.50 to 0.70
|
%
|
Internal Method |
Water Absorption (24 hr)
|
0.060
|
%
|
ASTM D570 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus 3
|
2500
|
MPa
|
ASTM D638 |
Tensile Modulus
|
2670
|
MPa
|
ISO 527-2/1 |
Tensile Strength 4 (Yield)
|
65.0
|
MPa
|
ASTM D638 |
Tensile Stress (Yield)
|
61.3
|
MPa
|
ISO 527-2/50 |
Tensile Strength 4 (Break)
|
53.1
|
MPa
|
ASTM D638 |
Tensile Stress (Break)
|
50.8
|
MPa
|
ISO 527-2/50 |
Tensile Elongation 4 (Yield)
|
4.0
|
%
|
ASTM D638 |
Tensile Strain (Yield)
|
4.3
|
%
|
ISO 527-2/50 |
Tensile Elongation 4 (Break)
|
15
|
%
|
ASTM D638 |
Tensile Strain (Break)
|
21
|
%
|
ISO 527-2/50 |
Flexural Modulus
|
ASTM D790 | ||
50.0 mm Span 5
|
2700
|
MPa
|
|
100 mm Span 6
|
2400
|
MPa
|
|
Flexural Modulus 7
|
2560
|
MPa
|
ISO 178 |
Flexural Strength 7, 8
|
99.5
|
MPa
|
ISO 178 |
Flexural Strength
|
ASTM D790 | ||
Yield, 50.0 mm Span 5
|
100
|
MPa
|
|
Yield, 100 mm Span 6
|
98.0
|
MPa
|
|
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact
|
ASTM D256 | ||
-30°C
|
110
|
J/m
|
|
23°C
|
180
|
J/m
|
|
Notched Izod Impact Strength 9 (23°C)
|
15
|
kJ/m2
|
ISO 180/1A |
Unnotched Izod Impact (23°C)
|
2600
|
J/m
|
ASTM D4812 |
Instrumented Dart Impact (23°C, Total Energy)
|
49.7
|
J
|
ASTM D3763 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under
Load
|
ASTM D648 | ||
0.45 MPa, Unannealed, 3.20
mm
|
127
|
°C
|
|
0.45 MPa, Unannealed, 6.40
mm
|
129
|
°C
|
|
Heat Deflection Temperature 10 (0.45 MPa, Unannealed,
100 mm Span)
|
129
|
°C
|
ISO 75-2/Be |
Deflection Temperature Under
Load
|
ASTM D648 | ||
1.8 MPa, Unannealed, 3.20
mm
|
113
|
°C
|
|
1.8 MPa, Unannealed, 6.40
mm
|
118
|
°C
|
|
Heat Deflection Temperature 10 (1.8 MPa, Unannealed,
100 mm Span)
|
115
|
°C
|
ISO 75-2/Ae |
Vicat Softening
Temperature
|
|||
--
|
132
|
°C
|
ISO 306/B50 |
--
|
135
|
°C
|
ISO 306/B120 |
CLTE - Flow (-40 to 40°C)
|
0.000080
|
cm/cm/°C
|
ASTM E831 |
CLTE - Transverse (-40 to 40°C)
|
0.000088
|
cm/cm/°C
|
ASTM E831 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
> 1.0E+15
|
ohm
|
ASTM D257 |
Volume Resistivity
|
2.3E+16
|
ohm·cm
|
ASTM D257 |
Dielectric Strength (3.20 mm, in Oil)
|
18
|
kV/mm
|
ASTM D149 |
Dielectric Constant
|
ASTM D150 | ||
50 Hz
|
2.52
|
|
|
60 Hz
|
2.52
|
|
|
1 MHz
|
2.46
|
|
|
Dissipation Factor
|
ASTM D150 | ||
50 Hz
|
0.0034
|
|
|
60 Hz
|
0.0034
|
|
|
1 MHz
|
0.0021
|
|
|
Arc Resistance (PLC) 11
|
PLC 6
|
|
ASTM D495 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating - UL
|
UL 94 | ||
5.99 mm
|
V-0
|
|
|
1.47 mm
|
V-1
|
|