* 厂家(产地): | 德国拜耳/泰国拜耳/上海拜耳 | * 牌号: | T65 |
* 销售方式: | 品牌经销 | 备注说明: | 原厂正牌,货到付款 |
* 地区: | 全国 |
德国拜耳/泰国拜耳/上海拜耳PC/ABS T65 000000 原厂原包,货真价实,价格优惠,亲!~
专业供应PC+ABS塑胶原料:防火PC+ABS,阻燃PC+ABS,耐高温PC+ABS,耐热PC+ABS,抗冲击PC+ABS,食品级PC+ABS,高冲击PC+ABS,抗紫外线PC+ABS,低粘度PC+ABS,电镀级PC+ABS,加玻纤PC+ABS,耐低温PC+ABS,高流动PC+ABS,无卤PC+ABS,无溴PC+ABS,注塑级PC+ABS,等塑胶原料。
德国拜耳/泰国拜耳/上海拜耳PC/ABS T65 000000物性表
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.13
|
g/cm³
|
ISO 1183 |
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)
|
15.0
|
cm³/10min
|
ISO 1133 |
Molding Shrinkage 2
|
ISO 2577 | ||
Across Flow: 260°C, 3.00 mm
|
0.65 to 0.85
|
%
|
|
Flow: 260°C, 3.00 mm
|
0.65 to 0.85
|
%
|
|
Water Absorption (Saturation, 23°C)
|
1.0
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.20
|
%
|
ISO 62 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
2200
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Yield, 23°C)
|
52.0
|
MPa
|
ISO 527-2/50 |
Tensile Stress (Break, 23°C)
|
52.0
|
MPa
|
ISO 527-2/50 |
Tensile Strain (Yield, 23°C)
|
4.8
|
%
|
ISO 527-2/50 |
Tensile Strain (Break, 23°C)
|
> 50
|
%
|
ISO 527-2/50 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact Strength
|
ISO 180/A | ||
-30°C
|
35
|
kJ/m²
|
|
23°C
|
45
|
kJ/m²
|
|
Unnotched Izod Impact Strength
|
ISO 180 | ||
-30°C
|
No Break
|
|
|
23°C
|
No Break
|
|
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
124
|
°C
|
ISO 75-2/B |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
103
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
|||
--
|
119
|
°C
|
ISO 306/B50 |
--
|
121
|
°C
|
ISO 306/B120 |
CLTE - Flow (23 to 55°C)
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse (23 to 55°C)
|
0.000085
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+15
|
ohm
|
IEC 60093 |
Volume Resistivity (23°C)
|
1.0E+15
|
ohm·cm
|
IEC 60093 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating (0.850 mm)
|
HB
|
|
UL 94 |
Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
Melt Viscosity (260°C, 1000 sec^-1)
|
210
|
Pa·s
|
ISO 11443-A |