台湾奇美PC/ABS PC-345 英文物性表
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.10
|
g/cm³
|
ASTM D792 |
Density
|
1.10
|
g/cm³
|
ISO 1183 |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)
|
20
|
g/10 min
|
ASTM D1238 |
Melt Volume-Flow Rate (MVR) (260°C/3.8 kg)
|
13.0
|
cm³/10min
|
ISO 1133 |
Molding Shrinkage - Flow
|
0.40 to 0.60
|
%
|
ASTM D955 |
Water Absorption (23°C, 24 hr)
|
0.40
|
%
|
ASTM D570 |
Spiral Flow Length 2 (260°C)
|
119
|
mm
|
Internal Method |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Strength (Yield, 23°C)
|
49.0
|
MPa
|
ASTM D638 |
Tensile Stress (Yield)
|
45.0
|
MPa
|
ISO 527-2/50 |
Tensile Stress (Break)
|
39.0
|
MPa
|
ISO 527-2/50 |
Tensile Elongation (Break, 23°C)
|
85
|
%
|
ASTM D638 |
Tensile Strain (Break)
|
80
|
%
|
ISO 527-2/50 |
Flexural Modulus (23°C)
|
2260
|
MPa
|
ASTM D790 |
Flexural Modulus 3
|
2300
|
MPa
|
ISO 178 |
Flexural Strength (23°C)
|
73.5
|
MPa
|
ASTM D790 |
Flexural Strength 3
|
75.0
|
MPa
|
ISO 178 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact (3.18 mm)
|
480
|
J/m
|
ASTM D256 |
Notched Izod Impact Strength
|
39
|
kJ/m²
|
ISO 180/1A |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Rockwell Hardness (R-Scale)
|
108
|
|
ASTM D785 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
95.0
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
95.0
|
°C
|
ISO 75-2/A |
Heat Deflection Temperature (1.8 MPa, Annealed)
|
106
|
°C
|
ISO 75-2/A |
Vicat Softening Temperature
|
125
|
°C
|
ASTM D1525 4 |
Vicat Softening Temperature
|
|||
--
|
125
|
°C
|
ISO 306/A50 |
--
|
110
|
°C
|
ISO 306/B50 |
CLTE - Flow (40 to 100°C)
|
0.000060 to 0.000080
|
cm/cm/°C
|
ASTM D696 |
RTI Elec
|
UL 746 | ||
1.50 mm
|
60.0
|
°C
|
|
3.00 mm
|
60.0
|
°C
|
|
RTI Imp
|
UL 746 | ||
1.50 mm
|
60.0
|
°C
|
|
3.00 mm
|
60.0
|
°C
|
|
RTI Str
|
UL 746 | ||
1.50 mm
|
60.0
|
°C
|
|
3.00 mm
|
60.0
|
°C
|
|
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Arc Resistance
|
PLC 6
|
|
ASTM D495 |
Comparative Tracking Index (CTI)
|
PLC 2
|
|
UL 746 |
High Amp Arc Ignition (HAI)
|
UL 746 | ||
1.50 mm
|
PLC 0
|
|
|
3.00 mm
|
PLC 0
|
|
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 2
|
|
UL 746 |
Hot-wire Ignition (HWI)
|
UL 746 | ||
1.50 mm
|
PLC 4
|
|
|
3.00 mm
|
PLC 3
|
|
|
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | ||
1.50 mm, ALL
|
HB
|
|
|
3.00 mm, ALL
|
HB
|
|
|
Flammability Classification
|
IEC 60695-11-10, -20 | ||
3.00 mm
|
HB40
|
|
|
1.50 mm
|
HB75
|
|
Processing Information | |||
Injection |
Nominal Value
|
Unit
|
|
Drying Temperature
|
80.0 to 100
|
°C
|
|
Drying Time
|
4.0
|
hr
|
|
Rear Temperature
|
200 to 230
|
°C
|
|
Middle Temperature
|
230 to 270
|
°C
|
|
Nozzle Temperature
|
220 to 260
|
°C
|
|
Mold Temperature
|
50.0 to 100
|
°C
|