德国拜耳/泰国拜耳/上海拜耳PC/ABS FR110 原厂原包，货真价实，价格优惠，亲！~
专业供应PC+ABS塑胶原料：防火PC+ABS,阻燃PC+ABS，耐高温PC+ABS，耐热PC+ABS，抗冲击PC+ABS，食品级PC+ABS，高冲击PC+ABS，抗紫外线PC+ABS，低粘度PC+ABS，电镀级PC+ABS，加玻纤PC+ABS，耐低温PC+ABS，高流动PC+ABS，无卤PC+ABS，无溴PC+ABS，注塑级PC+ABS，等塑胶原料。
德国拜耳/泰国拜耳/上海拜耳PC/ABS FR110物性表
| Physical | Value | Unit of Measure | Conditions | Test |
|---|---|---|---|---|
| Specific Gravity | 1.19 | sp gr | 23/23°C | ASTM D-792 |
| Melt Flow Rate | 35 | g/10min | 300°C/1.2 kg - 0 | ASTM D-1238 |
| Mold Shrink, Linear-Flow | 0.004 to 0.006 | in/in (cm/cm) | ASTM D-955 | |
| Mechanical | Value | Unit of Measure | Conditions | Test |
| Tensile Modulus | 380,000 (2.622) | psi (GPa) | ASTM D-638 | |
| Tensile Stress @ Yield | 8,700 (60.03) | psi (MPa) | ASTM D-638 | |
| Tensile Stress @ Break | 8,100 (55.89) | psi (MPa) | ASTM D-638 | |
| Tensile Elongation @ Yield | 4.0 | % | ASTM D-638 | |
| Tensile Elongation @ Break | 90 | % | ASTM D-638 | |
| FlexuralModulus | 390,000 (2.691) | psi (GPa) | ASTM D-790 | |
| Flexural Strength | 13,800 (95.22) | psi (MPa) | ASTM D-790 | |
| Impact | Value | Unit of Measure | Conditions | Test |
| Notched Izod Impact Strength | 14 (747.306) | ft-lbs/in (J/m) | 0.125" (3.2 mm), 73°F (22.7°C) | ASTM D-256 |
| Instrumented Dart Impact Energy | 456 (51.528) | in/lbs (Joules) | 0.1000" (2.54 mm), 73°F (22.7°C) | ASTM D-256 |
| Hardness | Value | Unit of Measure | Conditions | Test |
| Rockwell Hardness | 122 | R Scale | ASTM D-785 | |
| Thermal | Value | Unit of Measure | Conditions | Test |
| Deflection Temp Under Load | 203 (95) | °F (C°) | 264psi (1.82 MPa) Unannealed | ASTM D-648 |
| Deflection Temp Under Load | 212 (100) | °F (C°) | 66psi (0.46 MPa) Unannealed | ASTM D-648 |
| Coefficient of Thermal Expansion | 4.3 e-005 | in/in/°F | ASTM D-696 | |
| Vicat Softening Point | 226 (107.77) | °F (C°) | ASTM D-1525 | |
| Flammability | Value | Unit of Measure | Conditions | Test |
| LimitingOxygen Index | 30 | % | ASTM D-2863 | |
| UL 94 Flame Class | Rating | 0.0590" (1.498mm) | UL 94 | |
| UL 94 Flame Class | Rating | 0.0790" (2.0066mm) | UL 94 | |
| UL 94 Flame Class | HB | Rating | 0.0790" (1.498mm) | UL 94 |
| UL 94 Flame Class | HB | Rating | 0.1180" (2.997mm) | UL 94 |
| UL 94 Flame Class | HB | Rating | 0.1180" (2.997mm) | UL 94 |
| UL 746 | Value | Unit of Measure | Conditions | Test |
| Relative Temp Index Mechanical | 185 (85) | °F (C°) | Non-Impact, 0.0620" (1.5748mm) | UL 746 |
| Relative Temp Index Mech w/Impact | 185 (85) | °F (C°) | Impact, 0.0620" (1.5748mm) | UL 746 |
| Relative Temp Index Electrical | 203 (95) | °F (C°) | 0.0620" (1.5748mm) | UL 746 |
| Comparative Tracking Index | 300 | V | UL 746 | |
| High Volt Arc Track Rate | 5.91 | in/min | 0.1180" (2.997mm) | UL 746 |
| Hot Wire Ignition | 45 | Seconds | 0.0590" (1.498mm) | UL 746 |
| Hot Wire Ignition | 90 | Seconds | 0.1180" (2.997mm) | UL 746 |
| High Ampere Arc Ignition | 120 | Seconds | 0.0590" (1.498mm) | UL 746 |
| Electrical | Value | Unit of Measure | Conditions | Test |
| Dielectric Constant | 3.0 | @ 100 Hz, | ASTM D-150 | |
| Dielectric Constant | 2.9 | @ 1 Mhz, | ASTM D-150 | |
| Dielectric Strength | 760 | V/mil | Short time under oil @ 73°F (23°C) 0.062" (1.5748) | ASTM D-149 |
| Dissipation Factor | 0.004 | @ 100 Hz, | ASTM D-150 | |
| Dissipation Factor | 0.007 | @ 1 Mhz, | ASTM D-150 | |
| Surface Resistivity | 1014 | ohms | ASTM D-257 | |
| Volume Resistivity | 1015 | ohms-cm | Tinfoil Electrodes | ASTM D-257 |
| Arc Resistance | 90 | seconds | 0.1180" (2.997mm) | ASTM D-257 |
| Injection Molding Parameters | Value | Unit of Measure | Conditions | Test |
| Drying Temperature | 175 to 210 (79.44 to98.88) | °F (C°) | ||
| Drying Time | 3.0 to 4.0 | Hours | ||
| Suggested Max Moisture | 0.020 | % | ||
| Suggested Max Regrind | 20 | % | ||
| Rear Temperature | 430 to 445 (221.11 to 229) | °F (C°) | ||
| Middle Temperature | 435 to 455 (223.88 to 235) | °F (C°) | ||
| Front Temperature | 445 to 465 (229 to240.55) | °F (C°) | ||
| Nozzle Temperature | 485 to 505 (251.66 to 262.77) | °F (C°) | ||
| Processing (Melt) Temperature | 430 to 520 (221.11 to 271.11) | °F (C°) | ||
| Mold Temperature | 120 to 175 (48.88 to 79.44) | °F (C°) | ||
| Injection Pressure (melt) | 10,000 to 20,000 (69 to 138) | psi (MPa) | ||
| Back Pressure (melt) | 50 to 100 (344.74 to 963.9) | psi (KPa) | ||
| Screw Speed | 50 to 100 | rpm | ||
| Clamp Tonnage | 3.0 to 5.0 | Tons/in2 | ||
| Screw L/D Ratio | 20:1 | Ratio | ||
| Screw Compression Ratio | 2:1 to 3:1 | Ratio |