德国拜耳/泰国拜耳/上海拜耳PC/ABS T45 000000物性表
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1100
|
kg/m³
|
ISO 1183 2 |
Melt volume-flow rate (260°C/5.0 kg)
|
12.0
|
cm³/10min
|
ISO 1133 2 |
Molding Shrinkage
|
ISO 294-4 | ||
Across Flow: 3.00 mm
|
0.55 to 0.75
|
%
|
|
Flow: 3.00 mm
|
0.55 to 0.75
|
%
|
|
Water Absorption (Saturation)
|
0.70
|
%
|
ISO 62 2 |
Water Absorption (Equilibrium)
|
0.20
|
%
|
ISO 62 2 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile modulus
|
2100
|
MPa
|
ISO 527-2 2 |
Tensile Stress (Yield)
|
49.0
|
MPa
|
ISO 527-2 2 |
Tensile Stress (Break)
|
40.0
|
MPa
|
ISO 527-2/50 |
Tensile Strain (Yield)
|
3.7
|
%
|
ISO 527-2 2 |
Tensile Strain (Break)
|
50
|
%
|
ISO 527-2/50 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact Strength
|
ISO 180/A | ||
-30°C
|
36
|
kJ/m²
|
|
23°C
|
40
|
kJ/m²
|
|
Unnotched Izod Impact Strength
|
ISO 180/1U | ||
-30°C
|
No Break
|
|
|
23°C
|
No Break
|
|
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load (0.45 MPa)
|
112
|
°C
|
ISO 75-2 2 |
Deflection Temperature Under Load (1.8 MPa)
|
95.0
|
°C
|
ISO 75-2 2 |
Vicat Softening Temperature
|
112
|
°C
|
ISO 306/B120 |
Vicat Softening Temperature (50°C/h, B (50N))
|
110
|
°C
|
ISO 306 2 |
CLTE - Flow
|
0.000085
|
cm/cm/°C
|
ISO 11359-2 2 |
CLTE - Transverse
|
0.000090
|
cm/cm/°C
|
ISO 11359-2 2 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface resistivity
|
1.0E+16
|
ohm
|
IEC 60093 2 |
Volume resistivity
|
1.0E+14
|
ohm·m
|
IEC 60093 2 |
Electric strength
|
35
|
kV/mm
|
IEC 60243-1 2 |
Relative Permittivity (100 Hz)
|
3.10
|
|
IEC 60250 2 |
Relative Permittivity (1 MHz)
|
3.00
|
|
IEC 60250 2 |
Dissipation Factor (100 Hz)
|
0.0035
|
|
IEC 60250 2 |
Dissipation Factor (1 MHz)
|
0.0085
|
|
IEC 60250 2 |
Comparative tracking index
|
275
|
|
IEC 60112 2 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating (0.850 mm)
|
HB
|
|
UL 94 |